Mechanical properties investigations of the plasma sprayed coatings based on alumina powder

In this paper Al2O3 + 13 wt% TiO2 ceramic coatings manufactured by Atmospheric Plasma Spraying (APS) have been investigated. The commercial feedstock materials, Metco 6221 (top coat) and Amdry 4535 (bond coat) have been deposited on stainless steel coupons. The main goal of researches was to determine the influence of critical plasma spray parameters (CPSP) on structure and properties of the coatings. In present studies, the electrical power was a variable parameter. Coatings have been characterized in the terms of microstructure, topography, bond strength adhesion, fracture toughness and wear resistance. As a result, it was observed, that coatings sprayed with higher value of the electrical power exhibit higher mechanical properties due to better cohesion as well as higher melting degree.

W artykule zbadano powłoki ceramiczne Al2O3 + 13% wag. TiO2 wytwarzane przez atmosferyczne natryskiwanie plazmowe (APS). Handlowe materiały wsadowe, Meteo 6221 (warstwa wierzchnia) i Amdry 4535 (warstwa wiążąca) zostały osadzone na próbkach ze stali nierdzewnej. Głównym celem badań było określenie wpływu krytycznych parametrów natrysku plazmowego (CPSP) na strukturę i właściwości powłok. W obecnych badaniach moc elektryczna była zmiennym parametrem. Powłoki scharakteryzowano pod względem mikrostruktury, topografii, przyczepności siły wiązania, odporności na pękanie i odporności na zużycie. W rezultacie zaobserwowano, że powłoki natryskiwane wyższą wartością mocy elektrycznej wykazują wyższe właściwości mechaniczne ze względu na lepszą spójność, a także wyższy stopień topnienia.