The influence of the carbon equivalent on the weldability of high-strength low-alloy steel in the water environment

From many years, the high strength low alloy steels are often used for offshore constructions. This constructions, due to the environment in which they work, require more frequent repairs than the constructions from the land. For economic reasons, repairs take place in the underwater conditions, however water significantly decreases the weldability of steel. The paper presents the results of the CTS weldability test for S460ML and S460 steels, which have a similar value of the yield point, but different carbon equivalent (CeMIS) values. The welded joints were cut into specimens, which were then subjected to Vickers HV10 hardness measurements. The experiment has shown that as the CeMIS value increases, the hardness in the heat affected zone (HAZ) of joints and in the weld metal increases.

Z roku na rok coraz większe zastosowanie na konstrukcje offshore znajdują stale o podwyższonej wytrzymałości. Konstrukcje takie, ze względu na środowisko, w którym pracują wymagają częstszych napraw, niż w przypadku konstrukcji lądowych. Ze względów ekonomicznych naprawy odbywają się w warunkach podwodnych, jednakże woda znacząco pogarsza spawalność stali. W pracy przedstawiono wyniki próby spawalności CTS dla stało S460ML i S460, które posiadają zbliżoną wartość granicy plastyczności, jednak różnią się wielkością równoważnika węgla (CeMIS). Wykonane złącza pocięto na próbki, które następnie poddano pomiarom twardości metodą Vickersa HV10. Zrealizowane badania pokazały, iż wraz ze wzrostem wartości CeMIS zwiększa się twardość w strefie wpływu ciepła (SWC) złączy oraz w metalu spoiny.