Characterization and production of Turkish nepheline syenites for industrial applications

Tytuł:
Characterization and production of Turkish nepheline syenites for industrial applications
Autorzy:
Kangal, Murat Olgaç
Bulut, Gülay
Yeşilyur, Zeynep
Basturkcu, Huseyin
Burat, Fırat
Powiązania:
https://bibliotekanauki.pl/articles/110774.pdf
Data publikacji:
2019
Wydawca:
Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
Tematy:
nepheline syenite
flotation
leaching
glass
ceramics
Źródło:
Physicochemical Problems of Mineral Processing; 2019, 55, 3; 605-616
1643-1049
2084-4735
Język:
angielski
Prawa:
Wszystkie prawa zastrzeżone. Swoboda użytkownika ograniczona do ustawowego zakresu dozwolonego użytku
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
Nepheline syenite, which is a silica-poor crystalline rock, competes with feldspar in applications such as glass, ceramic filler, and pigment industries. While its appearance is medium coarse granular like granite, main differences between them are nepheline syenite is silica poor, and contains high alumina and alkali content. Turkey has considerable nepheline syenite deposits in Kırşehir Region, and they contain 1.3% Fe2O3 on average, thus cannot be used unless beneficiated by flotation or/and magnetic separation. In this paper, physical and physicochemical experiments were carried out to improve the quality of nepheline syenite ore. After determinations of chemical, mineralogical, and properties of the sample, three different technologies such as flotation, magnetic separation, and leaching were applied on the ore sample, separately and combined. The obtained results showed that the magnetic separation alone could not produce a nepheline syenite concentrate assaying 0.45% Fe2O3. It was not also possible to obtain a nepheline concentrate less than 0.25% Fe2O3 adapting optimum flotation conditions. The best results were found in combination of the high intensity wet magnetic separation and flotation between -212+63 μm particle size, and a final concentrate with 0.20% Fe2O3 and 0.01% TiO2 was obtained. The leaching experiments were conducted to further decrease Fe2O3 content. Finally, a saleable nepheline syenite concentrate for tile, sanitary ware, electrode, glass, and fiberglass industries was obtained with 6.63% K2O, 9.02% Na2O, 0.15% Fe2O3, and 0.01% TiO2 by the weight of 63.9% at the end of the experiments.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies