The surface morphology, structure and hydrophobicity of low-and high-molecular weight poly(dimethylsiloxane) (PDMS) fluids physically adsorbed onto multi-walled carbon nanotubes (MWCNTs) at different weight percentages (5, 10, 20 and 40 wt.%), were studied employing X-ray diffraction (XRD), attenuated total reflectanceFouriertransforminfrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM) and measurements of contact angle with water. It was found that MWCNTs agglomerate forming voids between tubes of a broad range, while adsorption of the polymer from a hexane solution results in the expected wrapping of nanotubes withPDMS chains and, further, in filling voids, as represented by SEM data. ATR-FTIR was used to investigate the possible structural changes in the polymer nanocomposites. Based on the contact anglemeasurementsvia water drop shape analysis,MWCNTs/PDMS nanocomposites were characterizedas astable,superhydrophobic materials with the maximum contact angle (CA) equal to 152°at CPDMS=40wt.%.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00