This study investigates the production of high-quality MgCl2 from recycled waste magnesite powder with an average particle size of d50 0.079 mm using the HCl acid leaching method. The experimental parameters were, leaching temperature, leaching time, amount of the acid, liquid-to-solid ratio, scale-up factor, acid concentration, particle size and mixing speed. The experiments were performed under reproducible conditions. The results showed that optimum leaching parameters were: temperature of 70 °C, 180 min leaching time, 130 cm3 acid consumption, 3.6 cm3/g liquid-to-solid ratio, scale-up factor of 1, 10.17 M acid concentration, 0.079 mm average particle size and a mixing speed 60 rpm. Under these optimum conditions, the leaching yield was 96.72%. The produced MgCl2 solution contained 0.04% SiO2, 0.36% CaO, 0% Fe2O3, 0% Al2O3, 46.73% MgCl2, 52.87% L.O.I. and 99.60% MgCl2+L.O.I. (= MgCl2·6H2O). These results indicated that high-quality magnesium chloride can be produced from waste magnesite powder.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00