In this study, we investigated linear attenuation coefficient (μ ), half value layer, tenth value layer at 243, 344, 866, 1088, 1112, 1528 keV. Mechanical properties of cements containing nanosized powders (nano-SiO₂, nano-Fe₂O₃, nano-Al₂O₃) are obtained. According to compressive strength results nano-SiO₂ added cementitious material gave the highest strength. Moreover, all the nanopowders added samples showed higher compressive strength with respect to reference sample. The experimental linear mass attenuation coefficients μ , half value layer, tenth value layer for cementitious material were compared with theoretical values obtained using XCOM. The experimental results were found to be in good agreement with the theoretical values.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00