We investigated coercivity, total losses and complex permeability of sintered Fe-Co powder cores to detect magnetization processes performing in ac magnetic field. The Fe-Co solid solution alloy powders with 50:50 wt% ratio were prepared by 1, 15, and 20 h alloyed mixture of pure chemical elements in planetary ball mill. The resulting powder was subsequently sintered into a disk form. The compaction was performed at a pressure of 800 MPa for 5 min at temperatures of 400°C, 500°C and 600°C in vacuum oxidation protective atmosphere, with pressure of 5×10¯³ Pa. The best magnetic properties exhibit sample prepared from 1 h alloyed powder, compacted at 600°C.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00