Dental practice today used a lot of different materials. This paper evaluates tribological
and mechanical properties of two dental materials CeramX and I-Light. Tribological
analysisad of samples was conducted at temperature 37°C and in the environment
of artificial saliva. The wear rate was evaluated with a ball-on-disc tribotester, in accordance
to ASTM G-133 norm. The counterbodies were 6-mm-in-diameter Al2
O3
steel balls. The load of 2, 10 and 20 N was applied. The tests were conducted at 0.15
m/s sliding velocity over a sliding stroke of 1000 m. The changes in the value of the
following parameters were measured during the trials: friction coefficient, friction
force, temperature and wear depth. After completing the tribological tests the surface
of samples was carried out.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00