The corrosion behavior of the bulk glassy samples of Ca₆₅Mg₁₅Zn₂₀ alloy was studied by electrochemical measurements and immersion tests in a simulated body fluid, physiological fluid, and the Ringer solution. The results of immersion show that the volume of H₂ evolved after 2 h in simulated body fluid (29.8 ml/cm²) is the highest in comparison with the results of measurements conducted in physiological fluid (11.3 ml/cm²) and the Ringer solution (7.4 ml/cm²). The electrochemical measurements indicated a shift of the corrosion potential (E_{corr}) from -1.58 V for plate tested in a physiological fluid to -1.56 V and -1.54 V for samples immersed in the Ringer solution and simulated body fluid, adequately. The X-ray diffraction measurements were used to determine composition of corrosion products. The corrosion products were mainly identified to be calcium carbonates and calcium/magnesium hydroxides.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00