This paper characterizes mechanical properties of the technological subsurface layer produced by medium milling of EM AW-AlCu4MgSi(A) aluminium alloy in hardened state T451 using a ball-end cutter and subsequent roller burnishing using a nitride ceramic ball. It was revealed that ball burnishing operations performed on curvilinear milled surfaces allow obtaining the subsurface layer with a minimum strain-hardening effect and induced compressive residual stresses without visible microstructural changes. As a result, such functional properties of the subsurface layer as fatigue strength, bearing properties and contact strength along with a very smooth machined surface of the Sa roughness of about 0.02 µm can be ensured.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00