TiO2 attracts much interest because of its many potential applications. The use of titanium dioxide strongly depends on its polymorphic form: brookite, anatase, or rutile. Only rutile and anatase play an important role in industry. Anatase as a metastable form undergoes a non-reversible transformation into rutile. Understanding the kinetics of phase transformation and the processes of crystal growth of a material is essential for controlling its structure and, thus, its specific properties. The main purpose of this paper is to explain the anatase to rutile recrystallization kinetics in the modified TiO2 calcined from industrial hydrated titanium dioxide. The apparent activation energy of anatase to rutile transformation and the average size of titanium dioxide crystallites were determined for the unmodified TiO2 and TiO2 modified with P, K, Al, B, Zn, Zr, Ce, Sn, or Sb introduced in the amount of 0.5 mol% and 1.0 mol% when recalculated for their oxides. The growth of TiO2 crystallites during calcination was strongly inhibited by P, Ce and Zr, and inhibited to a lesser degree by Al, Sn and Sb. B and Zn did not affect the investigated process and K accelerated crystallites growth. The values of apparent activation energy depending on a modifier formed a relationship: Al
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00