New organic/inorganic hybrid fillers were obtained by mechanical modification of magnesium silicate with selected polyhedral oligomeric silsesquioxane and characterized afterwards. MgO ∙ SiO2 was precipitated in a water system. The effect of chemical modification of magnesium silicate surface on their physicochemical properties was determined. Functionalization was carried out with the use of different amount of (1-(3-hydroxypropyl)dimethylsiloxy- 3,5,7,9,11,13,15-hepta(isobutyl)pentacyclo-[9.5.1.13, 9.15, 15.17, 13]octasiloxane). The polypropylene composites of 0.5, 1.0 and 1.5 wt.% modified by 10 weight parts by the mass of the filler were also produced. For the obtained polypropylene composites measurements of the tensile strength, Young’s modulus and elongation at break were performed.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00