The paper presents the results of thermophysical properties of selected vermicular graphite cast iron with nominal chemical composition of 3.70 C; 2.30 Si; 0.44 Mn; 0.054 P; 0.015 S; 0.017 Mg (wt. %). The comparative studies of the alloy were performed using differential scanning calorimetry, dilatometry and laser flash analysis. The calorimetric investigations proved that upon the heating to melting temperature (~1200°C), four endothermic transformations take place:
1) ferromagnetic → paramagnetic at 742°C, 2) pearlite → austenite at 824.2°C, 3) allotropic transformation of bcc ferrite to fcc austenite at 802°C, 4) melting at 1173.1°C. The character of the dilatometric curve shows small deviation at the temperature above 810°C corresponding to the pearlite → austenite transformation. The values of thermal diffusivity and thermal conductivity change throughout the entire examined temperature range. Both curves showed a changeover from negative to positive trends between 700 and 800°C. This effect might be associated with the pearlite → austenite transformation.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00