The influence of the cyclic loading on the functional properties of NiTi was studied. Cylindrical specimens with a diameter
of 4 mm and a gage length of 12.5 mm were tested under uniaxial cyclic loading with control crosshead displacement at a temperature
of 0°С. The dependences of the stress and strain range as well as dissipation energy on the number of loading cycles at different initial
stress range were analysed. During the first 10 loading cycles, a rapid decrease in the strain range and energy dissipation was observed.
Dissipation energy was invariant to the loading cycles’ number at N > 20 cycles and to the stress range that did not exceed the martensite
finish stress level, was within the same scatter band and can be described by the single dependence. With the stress range growth
at N < 20 cycles from 509 to 740 MPa, the value of dissipation energy increases and that of relative dissipation energy decreases. Loss
coefficient, which characterises material damping ability, significantly decreases during the first 10 loading cycles and remains practically
unchanged up to the failure of the specimens. At the stabilisation area, the loss coefficient is almost non-sensitive towards the stress
range.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00