In the dissertation it has been shown, that so called „time-thermal treatment” (TTT) of the alloy in liquid state, as overheating the metal with around 250°C above the Tliq. and detaining it in this temperature for around 30 minutes, improves the mechanical properties (HB, Rm, R0,2). It was ascertained, that overheating the AlSi17Cu5Mg alloy aids the modification, resulting with microcrystalline structure. Uniform arrangement of the Si primeval crystals in the warp, and α(Al) solution type, supersaturated with alloying elements present in the base content (Cu, Mg) assures not only increased durability in the ambient temperature, but also at elevated temperature (250°C), what is an advantage, especially due to the use in car industry.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00