Modification of Ti-6Al-4V Alloy Surface by EPD-PEO Process in ZrSiO4 Suspension Modyfikacja powierzchni stopu Ti-6Al-4V metodą PEO-EPDw zawiesinie ZrSiO4
Investigations on the surface modification of the Ti-6Al-4V alloy by plasma electrolytic oxidation are reported here. The oxidation process was carried out in a solution containing a zirconium silicate (ZrSiO4) suspension and sodium hydroxide (NaOH). Anodising was realised at voltages in a range from 100 V to 250 V. It was found that the morphology of the sample surface did not change during the oxidation of the alloy at 100 V. Application of voltages higher than 100 V led to the incorporation of zirconium silicate into the formed oxide layer and to significant changes of the surface morphology.
W pracy przedstawiono wyniki badań nad modyfikacją powierzchni stopu Ti-6A1-4V metodą plazmowego utleniania elek- trochemicznego. Proces ten prowadzono w roztworze zawierającym zawiesinę krzemianu cyrkonu (ZrSiO4 oraz wodorotlenek sodu (NaOH). Anodowanie prowadzono w zakresie napięcia od 100 do 250 V. Stwierdzono, że zastosowanie napięcia 100 V nie powoduje zmian w morfologii powierzchni stopu. Natomiast zastosowanie napięcia wyższego od 100 V powoduje wbudowanie krzemianu cyrkonu w tworzącą się warstewką tlenową oraz znaczne zmiany w morfologii powierzchni stopu Ti-6A1-4V.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00