Composite cathodes contain Ba0.5Sr0.5Co0.8Fe0.2O3-σ and La0.6Sr0.4Co0.8Fe0.2O3-σ were tested in different configuration for
achieving cathode of area specific resistance lower than Ba0.5Sr0.5Co0.8Fe0.2O3-σ and La0.6Sr0.4Co0.8Fe0.2O3-σ cathodes. Electrodes were screen printed on samaria-doped ceria electrolyte half-discs and tested in the three electrode setup by the electrochemical impedance spectroscopy. Microstructure was observed by scanning electron microscopy. The lowest area specific resistance 0.46 and 2.77 Ω cm-2 at 700 °C and 600 °C respectively revealed composite cathode contain Ba0.5Sr0.5Co0.8Fe0.2O3-σ and La0.6Sr0.4Co0.8Fe0.2O3-σ in 1:1 weight ratio. The area specific resistance of this cathode is characterized by the lowest activation energy among tested cathodes.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00