In this study, the extrusion characteristics of Al-2Zn-1Cu-0.5Mg-0.5RE alloys at 450, 500, and 550°C were investigated for the high formability of aluminum alloys. The melt was maintained at 720°C for 20 minutes, then poured into the mold at 200°C and hot-extruded with a 12 mm thickness bar at a ratio of 38:1. The average grain size was 175.5, 650.1, and 325.9 μm as the extrusion temperature increased to 450, 500 and 550°C, although the change of the phase fraction was not significant as the extrusion temperature increased. Cube texture increased with the increase of extrusion temperature to 450, 500 and 550°C. As the extrusion temperature increased, the electrical conductivity increased by 47.546, 47.592 and 47.725%IACS, and the tensile strength decreased to 92.6, 87.5, 81.4 MPa. Therefore, the extrusion temperature of Al extrusion specimen was investigated to study microstructure and mechanical properties.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00