In the present study, mechanical properties of 0.25Li2O.2SiO2-0.75BaO.2SiO2 glass-ceramic were investigated. The trans-formations‘ temperatures were determined by DTA instrument. The optimum nucleation temperature was found to be 540°C. This suggested the crystallization temperatures as 675, 720 and 800°C. After carrying out crystallization heat treatments, Vickers indentation test was applied. In order to determine the indentation fracture toughness (KIC), crack half-length ‚c‘ of the samples was measured. To calculate KIC, Young’s modulus, E and the measured hardness, Hv were used. Using KIC and probability of fracture ‚P‘, ln ln[1/(1 − P)] – ln KIC graph was drawn based on the Weibull distribution equation. Consequently, Weibull modulus, ‚m‘ and scale parameter, ‚K0‘ were determined and compared with each other.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00