Tem Observation Of Age-Hardening Precipitation In Mg-Gd-Y Alloys As Different Gd/Y Ratio

In this study, the early stage of aging in Mg-Gd-Y alloys has been observed by transmission electron microscopy (TEM), high angle annular dark field – scanning transmission electron microscopy (HAADF-STEM) and calculations of images and electron density and bond overlap population (BOP) by first principal to understand the origin of precipitation in this alloy. The small hexagon of 0.37 nm is the first precipitate in this alloy, and this is the evidence of short range ordering of D0₁₉ structure. This is referred as the pre β”-phase. In the peak aged condition, β’ phase with bco structure was mainly observed.

W pracy przedstawiono mikroskopowe obserwacje TEM wczesnego etapu starzenia stopów Mg-Gd-Y. Ponadto badania prowadzono z użyciem skaningowej transmisyjnej mikroskopii elektronowej. Wykorzystano zjawisko niekoherentnego rozpraszania w ciemnym polu i materiał obrazowano przy pomocy detektora pierścieniowego, który zbiera elektrony rozproszone pod dużymi kątami (HAADF-STEM). Przeprowadzono także analizę obrazów, obliczenie gęstości elektronowej i ilości nakładających się wiązań w celu zrozumienia źródła wydzieleń w ww. stopie. Pierwszym wytrąceniem w stopie jest mały sześciokąt o wielkości 0,37 nm, a dowodem tego jest uporządkowanie krótkiego zasięgu struktury D0₁₉.