In the present study, the effect of tool rotational speed on microstructure and mechanical properties of friction stir welded
joints between commercially pure copper and 6351 Al alloy was carried out in the range of tool rotational speeds of 300-900 rpm
in steps of 150 rpm at 30 mm/minutes travel speed. Up to 450 rpm, the interface of the joints is free from intermetallics and Al4 Cu9
intermetallic has been observed at the stir zone. However, Al4 Cu9 intermetallic was observed both at the interface and the stir zone
at 600 rpm. At 750 and 900 rpm tool rotational speed, the layers of AlCu, Al2 Cu3 and Al4 Cu9 intermetallics were observed at the
interface and only Al4 Cu9 intermetallics has been observed in the stir zone. The maximum ultimate tensile strength of ~207 MPa
and yield strength of ~168 MPa along with ~6.2% elongation at fracture of the joint have been obtained when processed at 450
rpm tool rotational speed.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00