Purpose: This paper is focused on the works concerning on preparing zirconium oxide ceramic blocks recommended for CAD/CAM systems used in prosthetic dentistry for manufacturing fixed prosthetic restorations. Methods: Zirconium-yttrium-magnesium mixed ceramic oxides were prepared by sol-gel method via hydrolysis and condensation of zirconium alkoxide precursor (zirconium (IV) propoxide) with yttrium and magnesium nitrates diluted in 2-propanol. The aim of this work it was to obtain 2% mol yttria stabilized zirconia ceramic powders with magnesium as an additional tetragonal ZrO2 phase stabilizer in amount between 2÷6% mol (with 2% variable). Prepared gels were dried (24 h in 65°C). Obtained powders were mixed with binder (carboxymethyl cellulose) and uniaxial pressed in to a specimens with diameter 38 x 22 x 6 mm. Afterwards green bodies were sintered in range of temperature between 1350-1550°C. Powders and blocks were characterized by Scanning Electron Microscopy, Fourier Transform Infrared Spectroscopy, Specific Area Measurement. Results: Highly homogeneous powders with a low open porosity, was obtained. Prepared blocks after sintering showed numerous cracks. Nevertheless blocks was fine grained and show quite reproducible chemical composition. Conclusion: A sol gel wet chemical route of powder synthesis allow to obtain high homogenous ceramic materials with inconsiderable amount of pores with low variation in a diameter. In spite of a reproducible synthesis methods of a ceramic powders, applied to prepare green bodies procedure and sintering manner do not allowed to obtain free from cracks zirconia ceramics blocks.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00