Leaching of heavy metals (Zn, Pb, Cu, Ni and Cr) from hazardous waste originating from steel works (slag) has been investigated. Contaminant leaching behavior from monolithic waste materials in the function of time was examined. There was established the cumulative leaching of elements per surface area of waste material and the impact of the duration of the leachant contact with the waste on the leachability. The types of processes accompanying the release of heavy metals were determined as well. Surface wash-off and dissolution were dominant processes during the leaching of the analyzed elements. Chromium was the only element whose release from the sample was controlled by diffusion when subjected to leaching in a liquid of pH 7. Due to the low levels of heavy metal leaching in relation to their concentrations in the samples, it seems that longer duration of the tank test can contribute to the release of additional amounts of the heavy metals.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00