Extended X-ray absorption fine structure (EXAFS) spectroscopy offers additional experimental evidence to the solution of site occupancy problem in ternary NiAlX alloys. A study of local order in the stoichiometric Ni$\text{}_{3}$Al$\text{}_{1-x}$Fe$\text{}_{x}$ ternary alloys (x = 0.02, 0.05, 0.10, 0.15, and 0.25) by EXAFS at the K-edge of Fe in the energy range from 7000 eV to 7600 eV are presented. Three models of substitutional behavior are considered - the preferential substitution of Fe atoms in: 1) Ni sites, 2) Al sites, 3) both sites. Data analysis was performed with theoretical and experimentally determined scattered photoelectron phases and amplitudes. The results of the EXAFS analysis are consistent with the picture in which most of the Fe atoms substitute Al sites and less than 25% of Fe atoms substitute Ni sites. Alloys with more than 10 at% of Fe showed higher tendency for ordering than those containing less than 10 at% Fe.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00