This paper presents the results of an investigation into the: microstructure, magnetic properties and influence of annealing temperature on the magnetocaloric effect of Fe₈₂Zr₇Nb₂Cu₁B₈ alloy in the as-quenched and partially crystalline state. The microstructure was investigated using Mössbauer spectroscopy. The magnetocaloric effect was observed as a change in the magnetic entropy, which was calculated from isothermal magnetization curves. Fully-amorphous Fe₈₂Zr₇Nb₂Cu₁B₈ alloys, in the as-quenched state, exhibit a Curie temperature equal to (340±5) K. The transmission Mössbauer spectrum for the as-quenched Fe₈₂Zr₇Nb₂Cu₁B₈ alloy is typical for weak ferromagnets with the average hyperfine field of 9.86(2) T. For this alloy in the as-quenched state, the changes in maximum magnetic entropy occur near the Curie points and are equal to 0.95 J/(kg K). Also, the maximum magnetic entropy changes decrease after partial crystallization.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00