The corrosion action for bulk and thin Nd₂Fe₁₄B films magnets in different corrosion media was studied. The thin Nd-Fe-B films of 100 nm ≤ d ≤ 1000 nm were deposited on glass substrate by "flash" evaporation method. The structure and microstructure of the samples were studied by X-ray diffraction analysis, scanning electron microscopy. The temperature dependence of the magnetization before and after corrosion action was carried out by ponderomotive method in the temperature range 80 ≤ T ≤ 800 K. It is shown that the specific magnetizations of the thin Nd-Fe-B films with d ≥ 1000 nm are comparable to those measured for the powder samples. The values of the coercive and saturation fields were determined from the hysteresis loops measurements.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00