Mica glass-ceramic was prepared by sintering method from in the $SiO_2-Al_2O_3-MgO-K_2O-B_2O_3-F_2$ system. The sintering behavior and machinability of a glass-ceramic composition were examined. The starting materials were mixed and milled in an alumina ball mill for 2 h. Then the powders were sieved to obtain grain sizes smaller than 75 μm. For the shaping process, disc samples were prepared by pressing at 100 MPa. The pressed discs were sintered at temperatures in the range from 900 to 1200C for 2 h in an electric furnace using a heating rate of 5°C/min. X-ray diffraction analysis, scanning electron microscopy, and machinability tests for characterization were performed on sintered samples. The results showed that all samples exhibited similar phases formation and good machinability.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00