With the use of differential scanning calorimetry (DSC), the characteristic temperatures and enthalpy of phase transformations were defined for commercial AlSi9Cu3 cast alloy (EN AC-46000) that is being used for example for pressurized castings for automotive industry. During the heating with the speed of 10ºC∙min-1 two endothermic effects has been observed. The first appears at the temperature between 495 ºC and 534 ºC, and the other between 555 ºC and 631 ºC. With these reactions the phase transformation enthalpy comes up as +6 J g-1 and +327 J g-1. During the cooling with the same speed, three endothermic reactions were observed at the temperatures between 584 ºC and 471 ºC. The total enthalpy of the transitions is – 348 J g-1. Complimentary to the calorimetric research, the structural tests (SEM and EDX) were conducted on light microscope Reichert and on scanning microscope Hitachi S-4200. As it comes out of that, there are dendrites in the structure of α(Al) solution, as well as the eutectic (β) silicon crystals, and two types of eutectic mixture: double eutectic α(Al)+β(Si) and compound eutectic α+Al2Cu+β.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00