In this study, we investigated the effect of Fe addition (0, 0.25, 0.50 and 0.75 wt.%) on the microstructure, mechanical properties and electrical conductivity of as-cast and as-extruded Al-RE alloys. As the Fe element increased by 0 and 0.75wt.%, the phase fraction increased to 5.05, 5.76, 7.14 and 7.38 %. The increased intermetallic compound increased the driving force for recrystallization and grain refinement. The electrical conductivity of Al-1.0 wt.%RE alloy with Fe addition decreased to 60.29, 60.15, 59.58 and 59.13 % IACS. With an increase in the Fe content from 0 to 0.75 wt.% the ultimate tensile strength (UTS) of the alloy increased from 74.3 to 77.5 MPa. As the mechanical properties increase compared to the reduction of the electrical conductivity due to Fe element addition, it is considered to be suitable for fields requiring high electrical conductivity and strength.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00