Microstructure of Cast Ni-Cr-Al-C Alloy

Nickel based alloys, especially nickel based superalloys have gained the advantage over other alloys in the field of high temperature applications, and thus become irreplaceable at high temperature creep and aggressive corrosion environments, such as jet engines and steam turbines. However, the wear resistance of these alloys is insufficient at high temperatures. This work describes a microstructure of a new cast alloy. The microstructure consists of γ matrix strengthened by γ’ fine precipitates (dendrites) improving the high temperature strength and of Chromium Cr7C3 primary carbides (in interdendritic eutectics) which are designed to improve wear resistance as well as the high temperature strength.

Stopy na osnowie niklu, a w szczególności superstopy na osnowie niklu zyskały przewagę w stosunku do innych stopów metali na polu zastosowań w wysokiej temperaturze. Są niezastąpione w warunkach pełzania wysokotemperaturowego, a także agresywnym środowisku korozyjnym silników odrzutowych czy tez turbin parowych. Jednakże odporność na ścieranie tych stopów jest niewystarczalna do zastosowania tych materiałów w wysokiej temperaturze i warunkach ścierania. W niniejszej pracy opisano mikrostrukturę nowego stopu. Składa się ona z osnowy γ umocnionej fazą γ’ (dendryty) - zwiększającą wytrzymałość wysokotemperaturową, a także z pierwotnych węglików chromu Cr7C3 (w eutektykach międzydentrytycznych) - mających na celu zwiększyć zarówno odporność na ścieranie jak i wytrzymałość wysokotemperaturową.