This study manufactured Ti-6Al-4V alloy using one of the powder bed fusion 3D-printing processes, selective laser melting,
and investigated the effect of heat treatment (650°C/3hrs) on microstructure and impact toughness of the material. Initial microstructural
observation identified prior-β grain along the building direction before and after heat treatment. In addition, the material
formed a fully martensite structure before heat treatment, and after heat treatment, α and β phase were formed simultaneously.
Charpy impact tests were conducted. The average impact energy measured as 6.0 J before heat treatment, and after heat treatment,
the average impact energy increased by approximately 20% to 7.3 J. Fracture surface observation after the impact test showed
that both alloys had brittle characteristics on macro levels, but showed ductile fracture characteristics and dimples at micro levels.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00