Rare earth Nd-Fe-B, a widely used magnet composition, was synthesized in a shape of powders using gas atomization, a rapid
solidification based process. The microstructure and properties were investigated in accordance with solidification rate and densification.
Detailed microstructural characterization was performed by using scanning electron microscope (SEM) and the structural
properties were measured by using X-ray diffraction. Iron in the form of α-Fe phase was observed in powder of about 30 μm. It
was expected that fraction of Nd2 Fe14 B phase increased rapidly with decrease in powder size, on the other hand that of α-Fe phase
was decreased. Nd-rich phase diffused from grain boundary to particle boundary after hot deformation due to capillary action.
The coercivity of the alloy decreased with increase in powder size. After hot deformation, Nd2 Fe14 B phase tend to align to c-axis.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00