The grain boundary wetting phase transition in an industrial EZ33A cast alloy is studied. 12% of the grain boundaries are completely wetted at the temperature slightly higher than the eutectic transformation temperature (530°C). The fraction of wetted grain boundaries increases with temperature, reaches a maximum of 85% at 570°C, and does not change further until the alloy melts. In the as-cast state, the alloy has low ductile properties at the ambient temperature. The microstructure in the as-cast state corresponds to the wetting state at about 560°C, which indicates that the cooling rate in casting is almost equal to that in quenching. The volume and the surface fraction of the second phase and the hardness measured at the least wetted state of samples point toits good machinability. The wetting data are used to suggest a sequence of heat treatment and machining for processing EZ33A alloy parts.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00