In the present paper the structure and thermal properties of europium cerium oxides were investigated. The material for the
research was obtained via solid state synthesis. The initial powders: ceria CeO2 and europia Eu2O3 were mixed in 1:1 mass ratio
(non-stoichiometric proportion with the excess of CeO2) and milled. The sintering process was performed using high temperature
vacuum press at 1350°C. Calorimetric analysis was conducted both for initial powders and milled mixture. The structure, phase
composition and thermal diffusivity of obtained material were investigated in as-sintered condition. It was revealed that the obtained
material was multi-phase. Non-stoichiometric phases including Ce0.5Eu0.5O1.75 with fluorite type structure and different
lattice parameters were present. Thermal diffusivity decreased in the range from 25 to 900°C from 1.49 to 0.57 mm2 /s and then
increased to 0.70 mm2 /s at 1400°C.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00