Modification of the hypo-eutectic Al-Si alloys with an exothermic modifier

Results of studies on the modification of AlSi7Mg alloy with an exotherimc modifier are presented in the paper. MgO, Cr₂ O₃, Na₂O₂, NaNO₃, Na₂MoO₄ were used as modifiers in the amount of 0.05, 0.10, 0.15, 0.20 and 0.25%, and Cr₂O₃+Al, NaNO₃+Al, Na₂ MoO₄ +Al were applied as exothermic modifiers with Al as the reducing agent in the amount of 0.04-0.3%. The analyzed modifiers were incorporated in line with factorial design 2³. The Inmold modification method was applied. The microstructure of selected modified alloys was presented, and their tensile strength, percentage elongation and Brinell hardness number were given in graphic form. The results of the study indicate that the use of modifiers delivering an exothermic effect influences the effectiveness of silumin modification.

W pracy przedstawiono wyniki badań nad modyfikacja stopu AlSi7Mg modyfikatorem egzotermicznym. Do badań użyto, jako modyfikatorów związków MgO, Cr₂ O₃, Na₂O₂, NaNO₃, Na₂MoO₄ wprowadzanych w ilości 0.05, 0.10, 0.15, 0.20 and 0.25% oraz w postaci modyfikatora egzotermicznego z Al jako reduktorem Cr₂ O₃+Al, NaNO₃+Al i Na₂ MoO₄ +Al w ilości 0.04-0.3% wprowadzanych zgodnie z planem czynnikowym 2³. Modyfikacje prowadzono metodą Inmold. Przedstawiono wybrane mikrostruktury stopu po modyfikacji oraz w postaci graficznej wytrzymałość na rozciąganie, wydłużenie procentowe i twardość Brinella. Wykazano, że zastosowanie modyfikatora w postaci mieszanki dającej efekt egzotermiczny wpływa na efektywność modyfikacji siluminu.