The influence of densification time on the tensile strength and modulus of elasticity of birch veneers

The influence of densification time on the tensile strength and modulus of elasticity of birch veneers. The aim of the following study was to examine and compare tensile strength, modulus of elasticity, and thickness of birch (Betula pendula Roth) veneers modified by thermomechanical densification. Birch veneers were densified at the temperature of 100 °C at different times (ranges from 10 to 60 minutes). Tensile strength was tested longitudinally to the grain. As a result of this study change in tensile strength was observed for 60 minutes of densification. The rise in modulus of elasticity was also observed for 10, 20, 30, 50, and 60 minutes. The thickness of wooden veneers was changed significantly for each densification time.

Wpływ czasu zagęszczania na wytrzymałość na rozciąganie i moduł sprężystości fornirów brzozowych. Celem badań było określenie wybranych właściwości mechanicznych zagęszczonych fornirów z drewna brzozowego (Betula pendula Roth). W ramach badań przeprowadzono badanie wytrzymałości na rozciąganie wzdłuż włókien, a także modułu sprężystości oraz analizę zmiany grubości. Wyniki wskazują, że wytrzymałość na rozciąganie wzrosła znacząco dla próbek zagęszczanych przez czas 60 minut. Zaobserwowano również wzrost wartości modułu sprężystości dla próbek zagęszczanych przez okres 10, 20, 30, 50 i 60 minut. Zaobserwowano znaczącą zmianę grubości dla wszystkich czasów zagęszczania.