Dissolution of Si in Al-5 mass%Mg alloy melt by the reduction of SiO2 and its effect on microstructure formation of the alloy after solidification were investigated. Al-5 mass%Mg alloy without silica powder had approximately 0.05 mass%Si as an impurity. No significant difference in Si content was observed after the reaction with silica for 10 min, while the Si content increased up to about 0.12 mass% after 30 min. From the microstructure analysis and calculation of Scheil-Gulliver cooling, it was considered that as-cast microstructures of Al-5 mass%Mg-1 mass% SiO2 alloys had the distribution of eutectic phase particles, which are comprised of β-Al3Mg2 and Mg2Si phases. Based on the phase diagrams, only limited amount of Mg can be selectively removed by silica depending on the ratio of Si and Mg. Addition of silica of more than approximately 1.5 mass% in Al-5 mass%Mg alloy led to the formation of spinel and removal of both mg and Al from the melt.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00