Epitaxial, textured, and polycrystalline La$\text{}_{0.7}$Ca$\text{}_{0.3}$Mn O$\text{}_{3}$ films, having about 150 nm thickness, were prepared by pulsed laser deposition techniques onto (110) NdGaO$\text{}_{3}$, MgO and lucalox substrates and investigated using 10 ns duration, 0.5 ns rise time electrical pulses having amplitude up to 500 V. Electroresistance of the films [R(E)-R(0)]/R(0) was investigated up to 80 kV/cm electric field strengths in temperatures ranging from 300 K to 4.2 K. Strong (up to 93%) negative electroresistance was obtained in polycrystalline La$\text{}_{0.7}$Ca$\text{}_{0.3}$MnO$\text{}_{3}$ films prepared on MgO and lucalox substrates. The epitaxial films grown on NdGaO$\text{}_{3}$ substrate demonstrated only a small resistance change due to Joule heating induced by a current pulse. It was concluded that electroresistance manifests itself in strongly inhomogeneous manganites films exhibiting a large number of structural imperfections producing ferromagnetic tunnel junction nets.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00