The synthetic ZnAl$\text{}_{2}$O$\text{}_{4}$ spinels doped with Cr$\text{}^{3+}$ ions are prepared from ZnSO$\text{}_{4}$, Al$\text{}_{2}$(SO$\text{}_{4}$)$\text{}_{3}$, and Cr$\text{}_{2}$(SO$\text{}_{4}$)$\text{}_{3}$. The spinel single phase is detected from X-ray diffraction. Luminescence properties of Cr$\text{}^{3+}$ in ZnAl$\text{}_{2}$O$\text{}_{4}$ were studied by low temperature luminescence and decay measurements. Four luminescence lines at 14570, 14520, 14460, and 14330 cm$\text{}^{-1}$ were found to originate from structure distortion and the line at 14175 cm$\text{}^{-1}$ - from chromium pairs. The broad emission band at about 13540 cm$\text{}^{-1}$ is considered to arise from a new Cr$\text{}^{3+}$ center in ZnCr$\text{}_{2}$O$\text{}_{4}$.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00