Magnesium single crystals of three different orientations were deformed by tension at room temperature to investigate the geometrical criterion resulting from the Schmid law for activation of basal and non-basal slip systems. Changes of crystallographic orientations of investigated single crystals were systematically measured during deformation and the geometrical criterion was examined in respect to the changes of crystallographic orientations during deformation. The geometrical criterion itself failed to explain lack of activity of non-basal slip systems in the deformed magnesium single crystals. Therefore the ratio of activation volumes of soft to hard slip systems is considered to be introduced for a better understanding of the deformation in hcp metals.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00