Aluminum alloy AA5754 is used for many technical and industrial applications. Twin roll casting is unique among the casting processes in that it is a combined "solidification/deformation" technique. The simultaneous solidification and hot rolling produces characteristic microstructure with a fine cell size and intermetallic particle distribution with some residual structure. In the study, first AA5754 alloy (tread and plain sheet) strips were fabricated by using a twin-roll caster equipped with water-cooled steel-rolls. To reduce the thickness of the strip, cold rolling process was applied until strip thickness got 3 mm. After homogenization step the strips were cut in to smaller specimens and annealed at 260°C, 285°C, 310°C, 340°C, 370°C, 400°C, 430°C, 460°C, 490°C, 520°C for 3 hours to obtain the desired temper conditions. Mechanical properties were investigated after processes. Tensile, hardness and bending tests were applied to monitor the effect of annealing after cold rolling process.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00