We have studied the dependence of photodetector photocurrent on incident power density of light with anodization current and time. The fabrication of Al/PS/p-Si photodetector heterojunction PDH by electrochemical etching method ECE and semi-transparent Al films in thickness range of 80 nm are deposited by thermal evaporation on porous silicon layers to investigate the photocurrent -voltage characteristics of the PDH. When the anodization current varied from 20 to 60 mA, the photocurrent PC was increase according to the anodization parameters at 1.2 mw/cm2 power density. The results also show that the short current Isc and open circuit voltage Voc saturate at high power density. The difference in the value of Voc and Isc at different etching current density is related to the Si nano crystallites layer thickness and the porosity which itself is greatly affected by the etching current density.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00