The aim of presented paper is an investigation of the structure changes in AlSi9Cu alloy after remelting by a laser beam. Scanning transmission electron microscopy was applied for structure characterization and precipitates phase identification. In the raw material, precipitates were larger and during remelting such precipitates were dissolved and very fast crystallization came next. Observed precipitates are generally uniform: in size, shape, and chemical composition. Generally, after remelting precipitates are not uniformly distributed in the whole sample but areas with dense, nanometric precipitates are common. Numerous volumes with elongated Ti precipitates, identified as Ti(Al_{1-x}Si_{x})₃, were found. Observed precipitate can strongly affect material properties (even in a case of law Ti concentration) because it may act as a crystal nucleus for other phases.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00