The effect of mechanical properties on wear resistance of Si3
N4 – SiC composite materials with different portions
of SiC strengthening phase was investigated. Properties of monolithic silicon nitride were compared to ceramic
composites consisting of Si3
N4
matrix with 10 and 20 vol.% SiC. The SiC strengthening phase had a positive effect on the hardness of Si3
N4
– SiC ceramic composite materials. Wear resistance of tested ceramic materials was
mainly influenced by their fracture toughness. The highest wear resistance value was achieved for material with
the highest fracture toughness. Worn surfaces of all experimental ceramic materials were damaged by both microcutting and microcracking mechanism. Microcracking was the predominant wear mechanism mainly at ceramic
composites. The wear resistance of SiC-Si3
N4
ceramic composites can be described by the model W ~ HV/KIC.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00